Extended area of sputter deposited N-type and P-type thermoelectric legs in a flexible thin-film based thermoelectric device

ABSTRACT

A thin-film based thermoelectric module includes a flexible substrate, a number of electrically conductive pads disposed on the flexible substrate, and a number of pairs of N-type and P-type thermoelectric legs electrically in contact with one another formed on corresponding electrically conductive pads of the number of electrically conductive pads such that an area of each N-type thermoelectric leg and another area of each P-type thermoelectric leg are each more than an area of the corresponding electrically conductive pad to allow for extension thereof outside the corresponding electrically conductive pad. The flexible substrate is aluminum (Al) foil, a sheet of paper, teflon, plastic, a single-sided copper (Cu) clad laminate sheet, or a double-sided Cu clad laminate sheet, and has a dimensional thickness less than or equal to 25 μm. The thin-film based thermoelectric module is less than or equal to 100 μm in dimensional thickness.

CLAIM OF PRIORITY

This application is a continuation application of co-pending U.S. application Ser. No. 15/995,110 titled EXTENDED AREA OF SPUTTER DEPOSITED N-TYPE AND P-TYPE THERMOELECTRIC LEGS IN A FLEXIBLE THIN-FILM BASED THERMOELECTRIC DEVICE filed on May 31, 2018, which is a continuation-in-part application of U.S. application Ser. No. 15/869,017 titled FLEXIBLE ENCAPSULATION OF A FLEXIBLE THIN-FILM BASED THERMOELECTRIC DEVICE WITH SPUTTER DEPOSITED LAYER OF N-TYPE AND P-TYPE THERMOELECTRIC LEGS filed on Jan. 11, 2018, U.S. application Ser. No. 15/808,902 titled FLEXIBLE THIN-FILM BASED THERMOELECTRIC DEVICE WITH SPUTTER DEPOSITED LAYER OF N-TYPE AND P-TYPE THERMOELECTRIC LEGS filed on Nov. 10, 2017, U.S. application Ser. No. 14/564,072 titled VOLTAGE GENERATION ACROSS TEMPERATURE DIFFERENTIALS THROUGH A THERMOELECTRIC LAYER COMPOSITE filed on Dec. 8, 2014, which is a conversion application of U.S. Provisional Application No. 61/912,561 also titled VOLTAGE GENERATION ACROSS TEMPERATURE DIFFERENTIALS THROUGH A THERMOELECTRIC LAYER COMPOSITE filed on Dec. 6, 2013, U.S. application Ser. No. 14/711,810 titled ENERGY HARVESTING FOR WEARABLE TECHNOLOGY THROUGH A THIN FLEXIBLE THERMOELECTRIC DEVICE filed on May 14, 2015 and issued as U.S. Pat. No. 10,141,492 on Nov. 27, 2018, and U.S. application Ser. No. 15/368,683 titled PIN COUPLING BASED THERMOELECTRIC DEVICE filed on Dec. 5, 2016 and issued as U.S. Pat. No. 10,290,794 on May 14, 2019. The contents of the aforementioned applications are incorporated by reference in entirety thereof.

FIELD OF TECHNOLOGY

This disclosure relates generally to thermoelectric devices and, more particularly, to extended area of sputter deposited N-type and P-type thermoelectric legs in a flexible thin-film based thermoelectric device.

BACKGROUND

A thermoelectric device may be formed from alternating N and P elements/legs made of semiconducting material on a rigid substrate (e.g., alumina) joined on a top thereof to another rigid substrate/plate (e.g., again, alumina). In a typical bulk thermoelectric module/device, N-type thermoelectric legs and P-type thermoelectric legs may be bookended by top and bottom metal traces. Because of the typical long length of said N-type thermoelectric legs and P-type thermoelectric legs, there is no shunting during soldering of the metal traces.

However, as the height of the N-type thermoelectric legs and the P-type thermoelectric legs reduce in thin-film based thermoelectric devices, the top metal trace(s) may shunt the bottom metal trace(s) during deposition thereof.

SUMMARY

Disclosed are methods, a device and/or a system of extended area of sputter deposited N-type and P-type thermoelectric legs in a flexible thin-film based thermoelectric device.

In one aspect, a thin-film based thermoelectric module includes a flexible substrate, a number of electrically conductive pads disposed on the flexible substrate, and a number of pairs of N-type and P-type thermoelectric legs electrically in contact with one another formed on corresponding electrically conductive pads of the number of electrically conductive pads such that an area of each N-type thermoelectric leg and another area of each P-type thermoelectric leg are each more than an area of the corresponding electrically conductive pad to allow for extension thereof outside the corresponding electrically conductive pad. The flexible substrate is aluminum (Al) foil, a sheet of paper, teflon, plastic, a single-sided copper (Cu) clad laminate sheet, or a double-sided Cu clad laminate sheet, and has a dimensional thickness less than or equal to 25 μm. The thin-film based thermoelectric module is less than or equal to 100 μm in dimensional thickness.

In another aspect, a thin-film based thermoelectric module includes a flexible substrate, a number of electrically conductive pads disposed on the flexible substrate, and a number of pairs of N-type and P-type thermoelectric legs electrically in contact with one another formed on corresponding electrically conductive pads of the number of electrically conductive pads such that an area of each N-type thermoelectric leg and another area of each P-type thermoelectric leg are each more than an area of the corresponding electrically conductive pad to allow for extension thereof outside the corresponding electrically conductive pad.

The flexible substrate is Al foil, a sheet of paper, teflon, plastic, a single-sided Cu clad laminate sheet, or a double-sided Cu clad laminate sheet, and the flexible substrate has a dimensional thickness less than or equal to 25 μm. The thin-film based thermoelectric module is less than or equal to 100 μm in dimensional thickness. The thin-film based thermoelectric module is flexible enough to enable an array of thin-film based thermoelectric modules, each of which is equivalent to the thin-film based thermoelectric module, to be completely wrappable and bendable around a system element from which the array of the thin-film based thermoelectric modules is configured to derive thermoelectric power.

In yet another aspect, a thin-film based thermoelectric device includes an array of thin-film based thermoelectric modules, each of which is less than or equal to 100 μm in dimensional thickness and includes a flexible substrate, a number of electrically conductive pads disposed on the flexible substrate, and a number of pairs of N-type and P-type thermoelectric legs electrically in contact with one another formed on corresponding electrically conductive pads of the number of electrically conductive pads such that an area of each N-type thermoelectric leg and another area of each P-type thermoelectric leg are each more than an area of the corresponding electrically conductive pad to allow for extension thereof outside the corresponding electrically conductive pad. The flexible substrate is Al foil, a sheet of paper, teflon, plastic, a single-sided Cu clad laminate sheet, or a double-sided Cu clad laminate sheet, and has a dimensional thickness less than or equal to 25 μm.

Other features will be apparent from the accompanying drawings and from the detailed description that follows.

BRIEF DESCRIPTION OF THE DRAWINGS

The embodiments of this invention are illustrated by way of example and not limitation in the figures of the accompanying drawings, in which like references indicate similar elements and in which:

FIG. 1 is a schematic view of a thermoelectric device.

FIG. 2 is a schematic view of an example thermoelectric device with alternating P and N elements.

FIG. 3 is a top schematic view of a thermoelectric device component, according to one or more embodiments.

FIG. 4 is a process flow diagram detailing the operations involved in realizing a patterned flexible substrate of a thermoelectric device as per a design pattern, according to one or more embodiments.

FIG. 5 is a schematic view of the patterned flexible substrate of FIG. 4, according to one or more embodiments.

FIG. 6 is a schematic view of the patterned flexible substrate of FIG. 4 with N-type thermoelectric legs, P-type thermoelectric legs, a barrier layer and conductive interconnects, according to one or more embodiments.

FIG. 7 is a process flow diagram detailing the operations involved in sputter deposition of the N-type thermoelectric legs of FIG. 6 on the patterned flexible substrate (or, a seed metal layer) of FIG. 5, according to one or more embodiments.

FIG. 8 is a process flow diagram detailing the operations involved in deposition of the barrier layer of FIG. 6 on top of the sputter deposited pairs of P-type thermoelectric legs and the N-type thermoelectric legs of FIG. 6 and forming the conductive interconnects of FIG. 6 on top of the barrier layer, according to one or more embodiments.

FIG. 9 is a process flow diagram detailing the operations involved in encapsulating the thermoelectric device of FIG. 4 and FIG. 6, according to one or more embodiments.

FIG. 10 is a schematic view of a flexible thermoelectric device embedded within a watch strap of a watch completely wrappable around a wrist of a human being.

FIG. 11 is a schematic view of a flexible thermoelectric device wrapped around a heat pipe.

FIG. 12 is a schematic view of a thermoelectric device with elastomer encapsulation, according to one or more embodiments.

FIG. 13 is a schematic view of deposition of a barrier film prior to application of an elastomer to encapsulate the thermoelectric device of FIG. 12, according to one or more embodiments.

FIG. 14 is a schematic view of flexibility and bendability of an example thermoelectric device in accordance with the embodiment of FIG. 12.

FIG. 15 is a schematic view of an increased/extended area of an N-type thermoelectric leg and another increased/extended area of a P-type thermoelectric leg compared to an area of corresponding electrically conductive pads to ensure no shunting during deposition of conductive interconnects in the thermoelectric devices of FIGS. 6 and 8-14, according to one or more embodiments.

FIG. 16 is a process flow diagram detailing the operations involved in realizing a flexible thin-film based thermoelectric module with sputter deposited N-type and P-type thermoelectric legs having extended areas thereof, according to one or more embodiments.

Other features of the present embodiments will be apparent from the accompanying drawings and from the detailed description that follows.

DETAILED DESCRIPTION

Example embodiments, as described below, may be used to provide methods, a device and/or a system of extended area of sputter deposited N-type and P-type thermoelectric legs in a flexible thin-film based thermoelectric device. Although the present embodiments have been described with reference to specific example embodiments, it will be evident that various modifications and changes may be made to these embodiments without departing from the broader spirit and scope of the various embodiments.

FIG. 1 shows a thermoelectric device 100. Thermoelectric device 100 may include different metals, metal 1 102 and metal 2 104, forming a closed circuit. Here, a temperature difference between junctions of said dissimilar metals leads to energy levels of electrons therein shifted in a dissimilar manner. This results in a potential/voltage difference between the warmer (e.g., warmer junction 106) of the junctions and the colder (e.g., colder junction 108) of the junctions. The aforementioned conversion of heat into electricity at junctions of dissimilar metals is known as Seebeck effect.

The most common thermoelectric devices in the market may utilize alternative P and N type legs/pellets/elements made of semiconducting materials. As heat is applied to one end of a thermoelectric device based on P and N type elements, charge carriers thereof may be released into the conduction band. Electron (charge carrier) flow in the N type element may contribute to a current flowing from the end (hot end) where the heat is applied to the other end (cold end). Hole (charge carrier) flow in the P type element may contribute to a current flowing from the other end (cold end) to the end (hot end) where the heat is applied. Here, heat may be removed from the cold end to prevent equalization of charge carrier distribution in the semiconductor materials due to migration thereof.

In order to generate voltage at a meaningful level to facilitate one or more application(s), typical thermoelectric devices may utilize alternating P and N type elements (legs/pellets) electrically coupled in series (and thermally coupled in parallel) with one another, as shown in FIG. 2. FIG. 2 shows an example thermoelectric device 200 including three alternating P and N type elements 202 ₁₋₃. The hot end (e.g., hot end 204) where heat is applied and the cold end (e.g., cold end 206) are also shown in FIG. 2.

Typical thermoelectric devices (e.g., thermoelectric device 200) may be limited in application thereof because of rigidity, bulkiness and high costs (>$20/watt) associated therewith. Also, these devices may operate at high temperatures using active cooling. Exemplary embodiments discussed herein provide for a thermoelectric platform (e.g., enabled via roll-to-roll sputtering on a flexible substrate (e.g., plastic)) that offers a large scale, commercially viable, high performance, easy integration and inexpensive (<20 cents/watt) route to flexible thermoelectrics.

In accordance with the exemplary embodiments, P and N thermoelectric legs may be deposited on a flexible substrate (e.g., plastic) using a roll-to-roll process that offers scalability and cost savings associated with the N and P materials. In a typical solution, bulk legs may have a height in millimeters (mm) and an area in mm². In contrast, N and P bulk legs described in the exemplary embodiments discussed herein may have a height in microns (μm) and an area in the μm² to mm² range.

Examples of flexible substrates may include but are not limited to aluminum (Al) foil, a sheet of paper, teflon, plastic and a single/double-sided copper (Cu) clad laminate sheet. As will be discussed below, exemplary embodiments involve processes for manufacturing/fabrication of thermoelectric devices/modules that enable flexibility thereof not only in terms of substrates but also in terms of thin films/thermoelectric legs/interconnects/packaging. Preferably, exemplary embodiments provide for thermoelectric devices/modules completely wrappable and bendable around other devices utilized in specific applications, as will be discussed below. Further, exemplary embodiments provide for manufactured/fabricated thermoelectric devices/modules that are each less than or equal to 100 μm in dimensional thickness. Although exemplary embodiments discuss thermoelectric devices in general, it is clear that the aforementioned thermoelectric devices are preferably thin-film based thermoelectric devices.

FIG. 3 shows a top view of a thermoelectric device component 300, according to one or more embodiments. Here, in one or more embodiments, a number of sets of N and P legs (e.g., sets 302 _(1-M) including N legs 304 _(1-M) and P legs 306 _(1-M) therein) may be deposited on a substrate 350 (e.g., plastic, Cu clad laminate sheet) using a roll-to-roll process discussed above. FIG. 3 also shows a conductive material 308 _(1-M) contacting both a set 302 _(1-M) and substrate 350, according to one or more embodiments; an N leg 304 _(1-M) and a P leg 306 _(1-M) form a set 302 _(1-M), in which N leg 304 _(1-M) and P leg 306 _(1-M) electrically contact each other through conductive material 308 _(1-M). Terminals 370 and 372 may be electrically conductive leads to measure the potential difference generated by a thermoelectric device including thermoelectric device component 300.

Exemplary thermoelectric devices discussed herein may find utility in solar and solar thermal applications. As discussed above, traditional thermoelectric devices may have a size limitation and may not scale to a larger area. For example, a typical solar panel may have an area in the square meter (m²) range and the traditional thermoelectric device may have an area in the square inch range. A thermoelectric device in accordance with the exemplary embodiments may be of varying sizes and/or dimensions ranging from a few mm² to a few m².

Additionally, exemplary thermoelectric devices may find use in low temperature applications such as harvesting body heat in a wearable device, automotive devices/components and Internet of Things (IoT). Entities (e.g., companies, start-ups, individuals, conglomerates) may possess expertise to design and/or develop devices that require thermoelectric modules, but may not possess expertise in the fabrication and packaging of said thermoelectric modules. Alternately, even though the entities may possess the requisite expertise in the fabrication and packaging of the thermoelectric modules, the entities may not possess a comparative advantage with respect to the aforementioned processes.

In one scenario, an entity may create or possess a design pattern for a thermoelectric device. Said design pattern may be communicated to another entity associated with a thermoelectric platform to be tangibly realized as a thermoelectric device. It could also be envisioned that the another entity may provide training with regard to the fabrication processes to the one entity or outsource aspects of the fabrication processes to a third-party. Further, the entire set of processes involving Intellectual Property (IP) generation and manufacturing/fabrication of the thermoelectric device may be handled by a single entity. Last but not the least, the entity may generate the IP involving manufacturing/fabrication of the thermoelectric device and outsource the actual manufacturing/fabrication processes to the another entity.

All possible combinations of entities and third-parties are within the scope of the exemplary embodiments discussed herein.

FIG. 4 shows the operations involved in realizing a patterned flexible substrate (e.g., patterned flexible substrate 504 shown in FIG. 5) of a thermoelectric device 400 as per a design pattern (e.g., design pattern 502 shown in FIG. 5), according to one or more embodiments. In one or more embodiments, operation 402 may involve choosing a flexible substrate (e.g., substrate 350) onto which, in operation 404, design pattern 502 may be printed (e.g., through inkjet printing, direct write, screen printing) and etched onto the flexible substrate. In one or more embodiments, a dimensional thickness of substrate 350 may be less than or equal to 25 μm.

Etching, as defined above, may refer to the process of removing (e.g., chemically) unwanted metal (say, Cu) from the patterned flexible substrate. In one example embodiment, a mask or a resist may be placed on portions of the patterned flexible substrate corresponding to portions of the metal that are to remain after the etch. Here, in one or more embodiments, the portions of the metal that remain on the patterned flexible substrate may be electrically conductive pads, electrically conductive leads and terminals formed on a surface of the patterned flexible substrate. FIG. 5 shows a patterned flexible substrate 504 including a number of electrically conductive pads 506 _(1-N) formed thereon. Each electrically conductive pad 506 _(1-N) may be a flat area of the metal that enables an electrical connection.

Also, FIG. 5 shows a majority set of the electrically conductive pads 506 _(1-N) as including pairs 510 _(1-P) of electrically conductive pads 506 _(1-N) in which one electrically conductive pad 506 _(1-N) may be electrically paired to another electrically conductive pad 506 _(1-N) through an electrically conductive lead 512 _(1-P) also formed on patterned flexible substrate 504; terminals 520 ₁₋₂ (e.g., analogous to terminals 370 and 372) may also be electrically conductive leads to measure the potential difference generated by the thermoelectric device/module fabricated based on design pattern 502. The aforementioned potential difference may be generated based on heat (or, cold) applied at an end of the thermoelectric device/module.

It should be noted that the configurations of the electrically conductive pads 506 _(1-N), electrically conductive leads 512 _(1-P) and terminals 520 ₁₋₂ shown in FIG. 5 are merely for example purposes, and that other example configurations are within the scope of the exemplary embodiments discussed herein. It should also be noted that patterned flexible substrate 504 may be formed based on design pattern 502 in accordance with the printing and etching discussed above.

Example etching solutions employed may include but are not limited to ferric chloride and ammonium persulphate. Referring back to FIG. 4, operation 406 may involve cleaning the printed and etched flexible substrate. For example, acetone, hydrogen peroxide or alcohol may be employed therefor. Other forms of cleaning are within the scope of the exemplary embodiments discussed herein. In one or more embodiments, the aforementioned processes discussed in FIG. 4 may result in a dimensional thickness of electrically conductive pads 506 _(1-N), electrically conductive leads 512 _(1-P) and terminals 520 ₁₋₂ being less than or equal to 18 μm.

The metal (e.g., Cu) finishes on the surface of patterned flexible substrate 504 may oxidize over time if left unprotected. As a result, in one or embodiments, operation 408 may involve additionally electrodepositing a seed metal layer 550 including Chromium (Cr), Nickel (Ni) and/or Gold (Au) directly on top of the metal portions (e.g., electrically conductive pads 506 _(1-N), electrically conductive leads 512 _(1-P), terminals 520 ₁₋₂) of patterned flexible substrate 504 following the printing, etching and cleaning. In one or more embodiments, a dimensional thickness of seed metal layer 550 may be less than or equal to 5 μm.

In one example embodiment, surface finishing may be employed to electrodeposit seed metal layer 550; the aforementioned surface finishing may involve Electroless Nickel Immersion Gold (ENIG) finishing. Here, a coating of two layers of metal may be provided over the metal (e.g., Cu) portions of patterned flexible substrate 504 by way of Au being plated over Ni. Ni may be the barrier layer between Cu and Au. Au may protect Ni from oxidization and may provide for low contact resistance. Other forms of surface finishing/electrodeposition may be within the scope of the exemplary embodiments discussed herein. It should be noted that seed metal layer 550 may facilitate contact of sputter deposited N-type thermoelectric legs (to be discussed below) and P-type thermoelectric legs (to be discussed below) thereto.

In one or more embodiments, operation 410 may then involve cleaning patterned flexible substrate 504 following the electrodeposition. FIG. 6 shows an N-type thermoelectric leg 602 _(1-P) and a P-type thermoelectric leg 604 _(1-P) formed on each pair 510 _(1-P) of electrically conductive pads 506 _(1-N), according to one or more embodiments. In one or more embodiments, the aforementioned N-type thermoelectric legs 602 _(1-P) and P-type thermoelectric legs 604 _(1-P) may be formed on the surface finished patterned flexible substrate 504 (note: in FIG. 6, seed layer 550 is shown as surface finishing over electrically conductive pads 506 _(1-N)/leads 512 _(1-P); terminals 520 ₁₋₂ have been omitted for the sake of clarity) of FIG. 5 through sputter deposition.

FIG. 7 details the operations involved in sputter deposition of N-type thermoelectric legs 602 _(1-P) on the surface finished patterned flexible substrate 504 (or, seed metal layer 550) of FIG. 5, according to one or more embodiments. In one or more embodiments, the aforementioned process may involve a photomask 650 (shown in FIG. 6) on which patterns corresponding/complementary to the N-type thermoelectric legs 602 _(1-P) may be generated. In one or more embodiments, a photoresist 670 (shown in FIG. 6) may be applied on the surface finished patterned flexible substrate 504, and photomask 650 placed thereon. In one or more embodiments, operation 702 may involve sputter coating (e.g., through magnetron sputtering) of the surface finished patterned flexible substrate 504 (or, seed metal layer 550) with an N-type thermoelectric material corresponding to N-type thermoelectric legs 602 _(1-P), aided by the use of photomask 650. The photoresist 670/photomask 650 functions are well understood to one skilled in the art; detailed discussion associated therewith has been skipped for the sake of convenience and brevity.

In one or more embodiments, operation 704 may involve stripping (e.g., using solvents such as dimethyl sulfoxide or alkaline solutions) of photoresist 670 and etching of unwanted material on patterned flexible substrate 504 with sputter deposited N-type thermoelectric legs 602 _(1-P). In one or more embodiments, operation 706 may involve cleaning the patterned flexible substrate 504 with the sputter deposited N-type thermoelectric legs 602 _(1-P); the cleaning process may be similar to the discussion with regard to FIG. 4.

In one or more embodiments, operation 708 may then involve annealing the patterned flexible substrate 504 with the sputter deposited N-type thermoelectric legs 602 _(1-P); the annealing process may be conducted (e.g., in air or vacuum) at 175° C. for 4 hours. In one or more embodiments, the annealing process may remove internal stresses and may contribute stability of the sputter deposited N-type thermoelectric legs 602 _(1-P). In one or more embodiments, a dimensional thickness of the sputter deposited N-type thermoelectric legs 602 _(1-P) may be less than or equal to 25 μm.

It should be noted that P-type thermoelectric legs 604 _(1-P) may also be sputter deposited on the surface finished pattern flexible substrate 504. The operations associated therewith are analogous to those related to the sputter deposition of N-type thermoelectric legs 602 _(1-P). Obviously, photomask 650 may have patterns corresponding/complementary to the P-type thermoelectric legs 604 _(1-P) generated thereon. Detailed discussion associated with the sputter deposition of P-type thermoelectric legs 604 _(1-P) has been skipped for the sake of convenience; it should be noted that a dimensional thickness of the sputter deposited P-type thermoelectric legs 604 _(1-P) may also be less than or equal to 25 μm.

It should be noted that the sputter deposition of P-type thermoelectric legs 604 _(1-P) on the surface finished patterned flexible substrate 504 may be performed after the sputter deposition of N-type thermoelectric legs 602 _(1-P) thereon or vice versa. Also, it should be noted that various feasible forms of sputter deposition are within the scope of the exemplary embodiments discussed herein. In one or more embodiments, the sputter deposited P-type thermoelectric legs 604 _(1-P) and/or N-type thermoelectric legs 602 _(1-P) may include a material chosen from one of: Bismuth Telluride (Bi₂Te₃), Bismuth Selenide (Bi₂Se₃), Antimony Telluride (Sb₂Te₃), Lead Telluride (PbTe), Silicides, Skutterudites and Oxides.

FIG. 8 details operations involved in deposition of a barrier layer 672 (refer to FIG. 6) on top of the sputter deposited pairs of P-type thermoelectric legs 604 _(1-P) and N-type thermoelectric legs 602 _(1-P) and forming conductive interconnects 696 on top of barrier layer 672, according to one or more embodiments.

In one or more embodiments, operation 802 may involve sputter depositing barrier layer 672 (e.g., film) on top of the sputter deposited pairs of the P-type thermoelectric legs 604 _(1-P) and the N-type thermoelectric leg 602 _(1-P) discussed above. In one or more embodiments, barrier layer 672 may be electrically conductive and may have a higher melting temperature than the thermoelectric material forming the P-type thermoelectric legs 604 _(1-P) and the N-type thermoelectric legs 602 _(1-P). In one or more embodiments, barrier layer 672 may prevent corruption (e.g., through diffusion, sublimation) of one layer (e.g., the thermoelectric layer including the P-type thermoelectric legs 604 _(1-P) and the N-type thermoelectric legs 602 _(1-P)) by another layer. An example material employed as barrier layer 672 may include but is not limited to Cr, Ni or Au. Further, in one or more embodiments, barrier layer 672 may further aid metallization contact therewith (e.g., with conductive interconnects 696).

In one or more embodiments, a dimensional thickness of barrier layer 672 may be less than or equal to 5 μm. It is obvious that another photomask (not shown) analogous to photomask 650 may be employed to aid the patterned sputter deposition of barrier layer 672; details thereof have been skipped for the sake of convenience and clarity. In one or more embodiments, operation 804 may involve may involve curing barrier layer 672 at 175° C. for 4 hours to strengthen barrier layer 672. In one or more embodiments, operation 806 may then involve cleaning patterned flexible substrate 504 with barrier layer 672.

In one or more embodiments, operation 808 may involve depositing conductive interconnects 696 on top of barrier layer 672. In one example embodiment, the aforementioned deposition may be accomplished by screen printing silver (Ag) ink or other conductive forms of ink on barrier layer 672. Other forms of conductive interconnects 696 based on conductive paste(s) are within the scope of the exemplary embodiments discussed herein. As shown in FIG. 8, a hard mask 850 may be employed to assist the selective application of conductive interconnects 696 based on screen printing of Ag ink. In one example embodiment, hard mask 850 may be a stencil.

In one or more embodiments, the screen printing of Ag ink may contribute to the continued flexibility of the thermoelectric device/module and low contact resistance. In one or more embodiments, operation 810 may involve cleaning (e.g., using one or more of the processes discussed above) the thermoelectric device/module/formed conductive interconnects 696/barrier layer 672 and polishing conductive interconnects 696. In one example embodiment, the polishing may be followed by another cleaning process. In one or more embodiments, operation 812 may then involve curing conductive interconnects 696 at 175° C. for 4 hours to fuse the conductive ink into solid form thereof. In one or more embodiments, conductive interconnects 696 may have a dimensional thickness less than or equal to 25 μm.

FIG. 9 details the operations involved in encapsulating the thermoelectric device (e.g., thermoelectric module 970)/module discussed above, according to one or more embodiments. In one or more embodiments, operation 902 may involve encapsulating the formed thermoelectric module (e.g., thermoelectric module 970)/device (with barrier layer 672 and conductive interconnects 696) with an elastomer 950 to render flexibility thereto. In one or more embodiments, as shown in FIG. 9, the encapsulation provided by elastomer 950 may have a dimensional thickness of less than or equal to 15 μm. In one or more embodiments, operation 904 may involve doctor blading (e.g., using doctor blade 952) the encapsulation provided by elastomer 950 to finish packaging of the flexible thermoelectric device/module discussed above.

In one or more embodiments, the doctor blading may involve controlling precision of a thickness of the encapsulation provided by elastomer 950 through doctor blade 952. In one example embodiment, elastomer 950 may be silicone. Here, said silicone may be loaded with nano-size aluminum oxide (Al₂O₃) powder to enhance thermal conductivity thereof to aid heat transfer across the thermoelectric module.

In one or more embodiments, as seen above, all operations involved in fabricating the thermoelectric device/module (e.g., thermoelectric device 400) render said thermoelectric device/module flexible. FIG. 10 shows a flexible thermoelectric device 1000 discussed herein embedded within a watch strap 1002 of a watch 1004 completely wrappable around a wrist 1006 of a human being 1008; flexible thermoelectric device 1000 may include an array 1020 of thermoelectric modules 1020 _(1-J) (e.g., each of which is thermoelectric device 400) discussed herein. In one example embodiment, flexible thermoelectric device 1000 may serve to augment or substitute power derivation from a battery of watch 1004. FIG. 11 shows a flexible thermoelectric device 1100 discussed herein wrapped around a heat pipe 1102; again, flexible thermoelectric device 1100 may include an array 1120 of thermoelectric modules 1120 _(1-J) (e.g., each of which is thermoelectric device 400) discussed herein. In one example embodiment, flexible thermoelectric device 1100 may be employed to derive thermoelectric power (e.g., through array 1120) from waste heat from heat pipe 1102.

It should be noted that although photomask 650 is discussed above with regard to deposition of N-type thermoelectric legs 602 _(1-P) and a P-type thermoelectric legs 604 _(1-P), the aforementioned deposition may, in one or more other embodiments, involve a hard mask 690, as shown in FIG. 6. Further, it should be noted that flexible thermoelectric device 400/1000/1100 may be fabricated/manufactured such that the aforementioned device is completely wrappable and bendable around a system element (e.g., watch 1004, heat pipe 1102) that requires said flexible thermoelectric device 400/1000/1100 to perform a thermoelectric power generation function using the system element.

The abovementioned flexibility of thermoelectric device 400/1000/1100 may be enabled through proper selection of flexible substrates (e.g., substrate 350) and manufacturing techniques/processes that aid therein, as discussed above. Further, flexible thermoelectric device 1000/1100 may be bendable 360° such that the entire device may completely wrap around the system element discussed above. Still further, in one or more embodiments, an entire dimensional thickness of the flexible thermoelectric module (e.g., flexible thermoelectric device 400) in a packaged form may be less than or equal to 100 μm, as shown in FIG. 9.

Last but not the least, as the dimensions involved herein are restricted to less than or equal to 100 μm, the flexible thermoelectric device/module discussed above may be regarded as being thin-film based (e.g., including processes involved in fabrication thereof).

FIG. 12 shows a thermoelectric device 1200 (e.g., thermoelectric module 970, also refer to the thermoelectric device of FIG. 6) discussed herein with elastomer encapsulation, according to one or more embodiments. In one or more embodiments, elastomer 950 may be provided on top of conductive interconnects 696; in certain embodiments, the encapsulation provided through elastomer 950 may extend into physical spaces between adjacent N-type thermoelectric legs 602 _(1-P) and P-type thermoelectric legs 604 _(1-P) in a direction perpendicular to a plane of substrate 350.

FIG. 12 also shows Room Temperature Vulcanizing (RTV) silicone 1250 (example elastomer 950) applied evenly across a surface of the thermoelectric device of FIG. 6, according to one or more embodiments. In one or more embodiments, as conductive interconnects 696 may be discontinuous and/or the adjacent N-type thermoelectric legs 602 _(1-P) and P-type thermoelectric legs 604 _(1-P) may have physical spaces therebetween, one or more hard mask(s) (e.g., one or more stencil(s); similar to hard mask 690/850) with patterns corresponding to the thermoelectric device of FIG. 6 and the desired configuration of the encapsulation may be employed to apply said RTV silicone 1250 evenly across the surface of the thermoelectric device.

In one or more embodiments, following the application of RTV silicone 1250, thermoelectric device 1200/RTV silicone 1250 may be cured (e.g., curing 1204 on a hot plate 1206 or an oven 1208) at 150° C. to strengthen the formed layer. It should be noted that, in one or more other embodiments, RTV silicone 1250 may be mixed with a thinner (not shown; e.g., silicone fluid; other examples are within the scope of the exemplary embodiments discussed herein) to enable the resulting mixture to provide for a less than 10 μm thickness of the formed encapsulation layer (in general, as discussed above, the encapsulation layer may be less than or equal to 15 μm in thickness). In certain other embodiments, RTV silicone 1250 may be mixed with finely dispersed Alumina (Al₂O₃) particles (not shown) to improve thermal conductivity thereof. It should be noted that the encapsulation may not solely be based on the doctor blading discussed above. Other methods to accomplish the encapsulation such as spin coating are within the scope of the exemplary embodiments discussed herein.

It is obvious that it may be advantageous to use filler material (e.g., Al₂O₃) of a higher thermal conductivity and/or a higher volume fraction to drastically improve thermal conductivity of the resultant mixture of RTV silicone and said filler material without sacrificing the desired final thickness (e.g., the thinner the better) of the encapsulation. Also, it is obvious that elastomer 950 may not solely be limited to RTV silicone 1250. Varieties of market ready high thermally conductive materials (e.g., filler material) and elastomers (or rubber) may be available for use in thermoelectric device 1200 and, therefore, are within the scope of the exemplary embodiments discussed herein.

FIG. 13 shows deposition (e.g., through sputtering) of a barrier film 1302 (e.g., of Silicon Nitride (Si₃N₄), of Alumina (Al₂O₃)) prior to application of elastomer 950 (e.g., RTV silicone, an elastomer with thinner, an elastomer with filler material) to encapsulate thermoelectric device 1200, according to one or more embodiments. In one or more embodiments, barrier film 1302 may be deposited (e.g., on top of conductive interconnects 696) to reduce moisture/water vapor/oxygen pervasion into layers of thermoelectric device 1200. It is obvious that moisture barrier thin-films (e.g., barrier film 1302) other than those including Si₃N₄ and/or Al₂O₃ may be employed in thermoelectric device 1200 prior to encapsulation thereof.

In one or more embodiments, a photomask or a hard mask (e.g., analogous to photo mask 650/hard mask 850) with patterns corresponding to barrier film 1302/elastomer 950 may be employed in the abovementioned deposition of barrier film 1302. In one example implementation, a 1-2 μm Si₃N₄ film may be sputter deposited to provide hermetic sealing to the thermoelectric layers of thermoelectric device 1200 for passivation purposes; then, RTV silicone rubber material (example elastomer 950) may be placed evenly thereon (e.g., based on doctor blading) to encapsulate thermoelectric device 1200; for example, the RTV silicone rubber material may be provided/placed around the Si₃N₄ film. The encapsulated thermoelectric device 1200/example elastomer 950 may then be cured at 150° C. for a couple of hours to cross-link polymers therein and to provide sealing.

It should be noted that the exemplary embodiments discussed herein provide for encapsulating the thin-film flexible thermoelectric device 1200 into a state of permanent sealing; only output pads may be exposed. As discussed above, the encapsulation may be less than or equal to 15 μm in thickness (in one embodiment, the encapsulation may be less than 10 μm in thickness). The abovementioned process of encapsulation, in conjunction with other processes involved in fabrication/manufacturing of thermoelectric device 400/thermoelectric module 970/thermoelectric device 1200, may enable said device to stretch or bend based on the flexibility of the final product discussed above.

FIG. 14 shows flexibility and bendability of an example thermoelectric device 1200 manufactured in accordance with the processes discussed herein. The aforementioned flexibility and bendability may facilitate use of the example thermoelectric device 1200 in a variety of applications, some of which are discussed with reference to FIGS. 10-11.

In typical bulk thermoelectric modules, top and bottom metal traces (e.g., metal traces analogous to conductive interconnects 696 and seed layer 550) may be separated by thermoelectric legs that are generally more than 1 mm in height/length. Because of this significant length, the top and bottom metal traces may not come in contact with one another during soldering, thereby preventing shunting therebetween. In contrast, exemplary embodiments discussed herein provide for thermoelectric device 400/thermoelectric module 970/thermoelectric device 1200 with small N-type thermoelectric legs 602 _(1-P) and P-type thermoelectric legs 604 _(1-P). Therefore, in one or more embodiments, the small thermoelectric leg height/dimension may lead to the top metal trace shunting the bottom metal trace during metal deposition, thereby producing no voltage.

In order to avoid the above shunting, in one or more embodiments, the area of each of the N-type thermoelectric legs 602 _(1-P) and P-type thermoelectric legs 604 _(1-P) may be chosen to be larger than the area of corresponding electrically conductive pads 506 _(1-N). In other words, more area corresponding to N-type thermoelectric legs 602 _(1-P) and P-type thermoelectric legs 604 _(1-P) may cover electrically conductive pads 506 _(1-N) than required to ensure no shunting during deposition of conductive interconnects 696.

FIG. 15 shows extended (or, increased) area 1502 of an N-type thermoelectric leg 602 _(1-P) and another extended (or, increased) area 1504 of a P-type thermoelectric leg 604 _(1-P) compared to area 1506 of corresponding electrically conductive pads 506 _(1-N) to ensure no shunting during deposition of conductive interconnects 696, according to one or more embodiments. In the top view, the corresponding electrically conductive pads 506 _(1-N), the corresponding electrically conductive lead 512 _(1-P) and seed metal layer 550 underneath N-type thermoelectric leg 602 _(1-P) and P-type thermoelectric leg 604 _(1-P) are shown in dotted lines to illustrate that area 1502 and another area 1504 of N-type thermoelectric leg 602 _(1-P) and P-type thermoelectric leg 604 _(1-P) respectively extend outside (or, are greater than) area 1506 of the corresponding electrically conductive pads 506 _(1-N). This is also clearly shown in the front view of the specific element of the thermoelectric device (e.g., thermoelectric device 1200) illustrated in FIG. 15. It is obvious that the increased leg area concept extends to all sputter deposited N-type thermoelectric legs 602 _(1-P) and P-type thermoelectric legs 604 _(1-P) and corresponding electrically conductive pads 506 _(1-N) thereof in an exemplary thermoelectric device (e.g., thermoelectric device 1200) discussed herein.

FIG. 16 shows a process flow diagram detailing the operations involved in realizing a flexible thin-film based thermoelectric module (e.g., thermoelectric device 1200) with a sputter deposited layer of N-type (e.g., N-type thermoelectric legs 602 _(1-P)) and P-type (e.g., P-type thermoelectric legs 604 _(1-P)) thermoelectric legs having extended areas thereof, according to one or more embodiments.

In one or more embodiments, operation 1602 may involve forming the thin-film based thermoelectric module by sputter depositing pairs of N-type thermoelectric legs and P-type thermoelectric legs electrically in contact with one another on corresponding electrically conductive pads (e.g., conductive pads 506 _(1-N)) on a flexible substrate (e.g., substrate 350) such that an area (e.g., including area 1502) of each sputter deposited N-type thermoelectric leg and another area (e.g., including area 1504) of each sputter deposited P-type thermoelectric leg is more than an area (e.g., area 1506) of the corresponding electrically conductive pad to allow for extension thereof outside the corresponding electrically conductive pad. In one or more embodiments, the flexible substrate may be an Al foil, a sheet of paper, teflon, plastic, a single-sided Cu clad laminate sheet, or a double-sided Cu clad laminate sheet, and may have a dimensional thickness less than or equal to 25 μm.

In one or more embodiments, operation 1604 may involve rendering the formed thin-film based thermoelectric module flexible and less than or equal to 100 μm in dimensional thickness based on choices of fabrication processes with respect to layers of the formed thin-film based thermoelectric module including the sputter deposited N-type thermoelectric legs and the P-type thermoelectric legs. In one or more embodiments, operation 1606 may then involve encapsulating the formed thin-film based thermoelectric module with an elastomer (e.g., elastomer 950) to render the flexibility thereto.

In one or more embodiments, the elastomer encapsulation may have a dimensional thickness less than or equal to 15 μm. In one or more embodiments, the flexibility may enable an array (e.g., array 1020/1120) of thin-film based thermoelectric modules, each of which is equivalent to the thin-film based thermoelectric module formed on the flexible substrate with the elastomer encapsulation, to be completely wrappable and bendable around a system element from which the array of the thin-film based thermoelectric modules is configured to derive thermoelectric power.

In one or more embodiments, a layer of the formed thin-film based thermoelectric module including the sputter deposited N-type thermoelectric legs and the P-type thermoelectric legs may have a dimensional thickness less than or equal to 25 μm.

Although the present embodiments have been described with reference to specific example embodiments, it will be evident that various modifications and changes may be made to these embodiments without departing from the broader spirit and scope of the various embodiments. Accordingly, the specification and drawings are to be regarded in an illustrative rather than a restrictive sense. 

What is claimed is:
 1. A thin-film based thermoelectric module comprising: a flexible substrate; a plurality of electrically conductive pads disposed on the flexible substrate; and a plurality of pairs of N-type and P-type thermoelectric legs electrically in contact with one another formed on corresponding electrically conductive pads of the plurality of electrically conductive pads such that an area of each N-type thermoelectric leg and another area of each P-type thermoelectric leg are each more than an area of the corresponding electrically conductive pad to allow for extension thereof outside the corresponding electrically conductive pad, wherein the flexible substrate is one of: aluminum (Al) foil, a sheet of paper, teflon, plastic, a single-sided copper (Cu) clad laminate sheet, and a double-sided Cu clad laminate sheet, wherein the flexible substrate has a dimensional thickness less than or equal to 25 μm, and wherein the thin-film based thermoelectric module is less than or equal to 100 μm in dimensional thickness.
 2. The thin-film based thermoelectric module of claim 1, wherein the thin-film based thermoelectric module is flexible and less than or equal to 100 μm in dimensional thickness based on choices of fabrication processes with respect to layers thereof including the N-type thermoelectric legs and the P-type thermoelectric legs.
 3. The thin-film based thermoelectric module of claim 2, wherein the flexibility of the thin-film based thermoelectric module enables an array of thin-film based thermoelectric modules, each of which is equivalent to the thin-film based thermoelectric module, to be completely wrappable and bendable around a system element from which the array of the thin-film based thermoelectric modules is configured to derive thermoelectric power.
 4. The thin-film based thermoelectric module of claim 1, wherein the corresponding electrically conductive pads are formed through printing and etching a design pattern of metal onto the flexible substrate.
 5. The thin-film based thermoelectric module of claim 1, further comprising a barrier metal layer comprising one of: Cr, Ni and Au directly on top of the plurality of pairs of the N-type thermoelectric legs and the P-type thermoelectric legs to further aid metallization contact therewith.
 6. The thin-film based thermoelectric module of claim 5, further comprising conductive interconnects on top of the barrier metal layer.
 7. The thin-film based thermoelectric module of claim 6, wherein the conductive interconnects are deposited on the top of the barrier metal layer through screen printing conductive forms of ink on the barrier metal layer.
 8. A thin-film based thermoelectric module, comprising: a flexible substrate; a plurality of electrically conductive pads disposed on the flexible substrate; and a plurality of pairs of N-type and P-type thermoelectric legs electrically in contact with one another formed on corresponding electrically conductive pads of the plurality of electrically conductive pads such that an area of each N-type thermoelectric leg and another area of each P-type thermoelectric leg are each more than an area of the corresponding electrically conductive pad to allow for extension thereof outside the corresponding electrically conductive pad, wherein the flexible substrate is one of: Al foil, a sheet of paper, teflon, plastic, a single-sided Cu clad laminate sheet, and a double-sided Cu clad laminate sheet, wherein the flexible substrate has a dimensional thickness less than or equal to 25 μm, wherein the thin-film based thermoelectric module is less than or equal to 100 μm in dimensional thickness, and wherein the thin-film based thermoelectric module is flexible enough to enable an array of thin-film based thermoelectric modules, each of which is equivalent to the thin-film based thermoelectric module, to be completely wrappable and bendable around a system element from which the array of the thin-film based thermoelectric modules is configured to derive thermoelectric power.
 9. The thin-film based thermoelectric module of claim 8, wherein the thin-film based thermoelectric module is flexible and less than or equal to 100 μm in dimensional thickness based on choices of fabrication processes with respect to layers thereof including the N-type thermoelectric legs and the P-type thermoelectric legs.
 10. The thin-film based thermoelectric module of claim 8, wherein the corresponding electrically conductive pads are formed through printing and etching a design pattern of metal onto the flexible substrate.
 11. The thin-film based thermoelectric module of claim 8, further comprising a barrier metal layer comprising one of: Cr, Ni and Au directly on top of the plurality of pairs of the N-type thermoelectric legs and the P-type thermoelectric legs to further aid metallization contact therewith.
 12. The thin-film based thermoelectric module of claim 11, further comprising conductive interconnects on top of the barrier metal layer.
 13. The thin-film based thermoelectric module of claim 12, wherein the conductive interconnects are deposited on the top of the barrier metal layer through screen printing conductive forms of ink on the barrier metal layer.
 14. A thin-film based thermoelectric device comprising: an array of thin-film based thermoelectric modules, each of which is less than or equal to 100 μm in dimensional thickness and comprises: a flexible substrate; a plurality of electrically conductive pads disposed on the flexible substrate; and a plurality of pairs of N-type and P-type thermoelectric legs electrically in contact with one another formed on corresponding electrically conductive pads of the plurality of electrically conductive pads such that an area of each N-type thermoelectric leg and another area of each P-type thermoelectric leg are each more than an area of the corresponding electrically conductive pad to allow for extension thereof outside the corresponding electrically conductive pad, wherein the flexible substrate is one of: Al foil, a sheet of paper, teflon, plastic, a single-sided Cu clad laminate sheet, and a double-sided Cu clad laminate sheet, and wherein the flexible substrate has a dimensional thickness less than or equal to 25 μm.
 15. The thin-film based thermoelectric device of claim 14, wherein the each thin-film based thermoelectric module is flexible and less than or equal to 100 μm in dimensional thickness based on choices of fabrication processes with respect to layers thereof including the N-type thermoelectric legs and the P-type thermoelectric legs.
 16. The thin-film based thermoelectric device of claim 15, wherein the flexibility of the each thin-film based thermoelectric module enables the array of thin-film based thermoelectric modules to be completely wrappable and bendable around a system element from which the array of the thin-film based thermoelectric modules is configured to derive thermoelectric power.
 17. The thin-film based thermoelectric device of claim 14, wherein the corresponding electrically conductive pads of the each thin-film based thermoelectric module are formed through printing and etching a design pattern of metal onto the flexible substrate.
 18. The thin-film based thermoelectric device of claim 14, wherein the each thin-film based thermoelectric module further comprises a barrier metal layer comprising one of: Cr, Ni and Au directly on top of the plurality of pairs of the N-type thermoelectric legs and the P-type thermoelectric legs to further aid metallization contact therewith.
 19. The thin-film based thermoelectric device of claim 18, wherein the each thin-film based thermoelectric module further comprises conductive interconnects on top of the barrier metal layer.
 20. The thin-film based thermoelectric device of claim 19, wherein the conductive interconnects are deposited on the top of the barrier metal layer of the each thin-film based thermoelectric module through screen printing conductive forms of ink on the barrier metal layer. 